The Use of Crack-Tip Opening Displacement for Testing of the Hydrogen Embrittlement of High-Strength Steels

ISSN： 1068-820X

Source： Materials Science, Vol.40, Iss.6, 2004-11, pp. : 749-755

Disclaimer: Any content in publications that violate the sovereignty, the constitution or regulations of the PRC is not accepted or approved by CNPIEC.

Previous Menu Next

Abstract

Related content

Characteristics of hydrogen embrittlement, stress corrosion cracking and tempered martensite embrittlement in high-strength steels

By Eliaz

Engineering Failure Analysis, Vol. 9, Iss. 2, 2002-04 ,pp. : 167-184

Elsevier

Access to resources Recommend Favorite

Hydrogen Degradation of High-Strength Weldable Steels in Seawater

By Cwiek J.

Materials Science, Vol. 40, Iss. 6, 2004-11 ,pp. : 831-835

Springer Publishing Company

Access to resources Recommend Favorite

A Method for Measuring Current Values of the Crack-Tip Opening Displacement under Cyclic Loading

By Krasovskii A.Y. Pinyak I.S.

Strength of Materials, Vol. 34, Iss. 4, 2002-07 ,pp. : 322-333

Springer Publishing Company

Access to resources Recommend Favorite

Crack tip opening displacement estimation formulae for C(T) specimens

By Panontin T.L. Makino A. Williams J.F.

Engineering Fracture Mechanics, Vol. 67, Iss. 3, 2000-10 ,pp. : 293-301

Elsevier

Access to resources Recommend Favorite

Effect of Cyclic Loading on Crack Tip Opening Displacement in AMg6 Alloy

By Yasnii P.V. Galushchak M.P.

Strength of Materials, Vol. 33, Iss. 1, 2001-01 ,pp. : 58-61

Springer Publishing Company

Access to resources Recommend Favorite