Ring crack propagation in silicon nitride under rolling contact

Author： Wang Y.   Hadfield M.  

Publisher： Elsevier

ISSN： 0043-1648

Source： Wear, Vol.250, Iss.1, 2001-10, pp. : 282-292

Disclaimer: Any content in publications that violate the sovereignty, the constitution or regulations of the PRC is not accepted or approved by CNPIEC.

Previous Menu Next

Abstract

Related content

The influence of ring crack location on the rolling contact fatigue failure of lubricated silicon nitride: fracture mechanics analysis

By Wang Y.   Hadfield M.  

Wear, Vol. 243, Iss. 1, 2000-08 ,pp. : 167-174

Elsevier

Access to resources Recommend Favorite

Rolling contact fatigue failure modes of lubricated silicon nitride in relation to ring crack defects

By Wang Y.   Hadfield M.  

Wear, Vol. 225, Iss. 2, 1999-04 ,pp. : 1284-1292

Elsevier

Access to resources Recommend Favorite

The influence of ring crack location on the rolling contact fatigue failure of lubricated silicon nitride: experimental studies

By Wang Y.   Hadfield M.  

Wear, Vol. 243, Iss. 1, 2000-08 ,pp. : 157-166

Elsevier

Access to resources Recommend Favorite

Transient wear of silicon nitride in lubricated rolling contact

By Chao L.   Lakshminarayanan R.   Iyer N.   Lin G.   Shetty D.K.  

Wear, Vol. 223, Iss. 1, 1998-12 ,pp. : 58-65

Elsevier

Access to resources Recommend Favorite

Wear of steel in rolling contact with silicon nitride

By Lakshminarayanan R.   Chao L.   Iyer N.   Shetty D.K.  

Wear, Vol. 210, Iss. 1, 1997-09 ,pp. : 278-286

Elsevier

Access to resources Recommend Favorite