Numerical and experimental study of the circular cracks observed at the contact edges of the indentations of coated systems with soft substrates

Author： Souza R.M.   Sinatora A.   Mustoe G.G.W.   Moore J.J.  

Publisher： Elsevier

ISSN： 0043-1648

Source： Wear, Vol.251, Iss.1, 2001-10, pp. : 1337-1346

Disclaimer: Any content in publications that violate the sovereignty, the constitution or regulations of the PRC is not accepted or approved by CNPIEC.

Previous Menu Next

Abstract

Related content

Numerical stress analysis of rail rolling contact fatigue cracks

By Bogdanski S.   Olzak M.   Stupnicki J.  

Wear, Vol. 191, Iss. 1, 1996-01 ,pp. : 14-24

Elsevier

Access to resources Recommend Favorite

Experimental and numerical study on the self-stress design of tensegrity systems

By Shekastehband B.   Abedi K.   Dianat N.  

Meccanica, Vol. 48, Iss. 10, 2013-12 ,pp. : 2367-2389

Springer Publishing Company

Access to resources Recommend Favorite

A simple method for the assessment of the contact modulus for coated systems

By Bull S.J.  

Philosophical Magazine, Vol. 95, Iss. 16-18, 2015-06 ,pp. : 1907-1927

Taylor & Francis Ltd

Access to resources Recommend Favorite

Flaking failure in rolling contact fatigue caused by indentations on mating surface (I) - Reproduction of flaking failure accompanied by cracks extending bi-directionally relative to the load-movement

By Fujii Y.   Maeda K.  

Wear, Vol. 252, Iss. 9, 2002-05 ,pp. : 787-798

Elsevier

Access to resources Recommend Favorite

Flaking failure in rolling contact fatigue caused by indentations on mating surface (II) - Formation process of flaking failure accompanied by cracks extending bi-directionally relative to the load-movement

By Fujii Y.   Maeda K.  

Wear, Vol. 252, Iss. 9, 2002-05 ,pp. : 799-810

Elsevier

Access to resources Recommend Favorite