Viscoelastic interpretations of erosion performance of short aramid fibre reinforced vinyl ester resin composites

Author： Kumar Sandeep Satapathy Bhabani Patnaik Amar

ISSN： 0022-2461

Source： Journal of Materials Science, Vol.46, Iss.23, 2011-12, pp. : 7489-7500

Disclaimer: Any content in publications that violate the sovereignty, the constitution or regulations of the PRC is not accepted or approved by CNPIEC.

Previous Menu Next

Abstract

Short aramid fibre reinforced vinyl ester resin based isotropic composites are fabricated with varying fibre weight fractions (20–50 wt%). The composites were evaluated for their erosion performance under a dynamic set of variables such as impingement angle (30°–90°), impact velocity (43–76 m/s), erodent size (250–600 μm) and stand-off distance (55–85 mm) following design of experiments (DOE) based on Taguchi analysis approach. The thermo-mechanical attributes such as storage modulus, loss modulus and damping properties as viscoelastic responses of the composites were investigated in the temperature range of 0–180 °C for their possible interpretations regarding reinforcement efficiency and energy dissipation aspects relevant to erosion process. An interrelation between the full-width half-maxima (FWHM) of loss modulus peak and erosion rate has emerged indicating the erosion to be mainly controlled by the fibre–matrix interfacial characteristics. The eroded surface morphology investigation by scanning electron microscopy (SEM) revealed the nature of wear-craters, material damage mode and other qualitative attributes responsible in facilitating erosion of the composites.