Specimen Size Requirements for Two-parameter Fracture Toughness Testing

Author: Zhu X.   Chao Y.  

Publisher: Springer Publishing Company

ISSN: 0376-9429

Source: International Journal of Fracture, Vol.135, Iss.1-4, 2005-09, pp. : 117-136

Disclaimer: Any content in publications that violate the sovereignty, the constitution or regulations of the PRC is not accepted or approved by CNPIEC.

Previous Menu Next

Abstract

Using a single parameter fracture mechanics theory, a minimum specimen size requirement of min(a, b, b) >200J0 in tension and min(a, b, b) >25J0 in bending, where b is the thickness, b the remaining ligament and a is the crack length of the specimen, were derived [Shih and German (1981), International Journal of fracture 17, 27–43] which have provided the basis for modern fracture toughness testing procedures. Two-parameter fracture toughness testing including the constraint, on the other hand, is desirable since it offers a solution to the transferability issue. A size requirement for a valid two-parameter fracture toughness testing based on the J-A2 three-term solution was determined as min(a, b, b) > 11J0 [Chao and Zhu (1998), International Journal of fracture 89, 285–307] in which the limiting case is bend specimens under large scale yielding (LSY). Recent work by Chao et al. (2004, International Journal of fracture, 27, 283–302) has shown that the J-A2 dominance at a crack tip can be significantly enhanced for bending specimens under LSY if a modified J-A2 solution is adopted. This current paper further studies the size of the J-A2 dominant zone using the modified J-A2 solution for deep bend specimens with hardening from low to high and loading from SSY to LSY using finite element analysis. Based on the results, a rather relaxed specimen size requirement min(a, b, b) >6J0 is developed and recommended for a valid two-parameter fracture toughness testing using the J-A2 fracture criterion. Validity of the size requirement is demonstrated by using the experimental J-R curves from non-standard bending specimens for A285 steel.