Author: Kroupa A. Havránková J. Svoboda M. Coufalová M. Vřešt’ál J.
Publisher: Springer Publishing Company
ISSN: 1054-9714
Source: Journal of Phase Equilibria, Vol.22, Iss.3, 2001-05, pp. : 312-323
Disclaimer: Any content in publications that violate the sovereignty, the constitution or regulations of the PRC is not accepted or approved by CNPIEC.
Abstract
Relevant experimental phase equilibria were used with the THERMOCALC program to refine thermodynamic parameters for the low-temperature region, in the steels with composition 0.4 to 2.5 wt.% Cr, 0 to 1 wt.% Mo, and 0 to 0.5 wt.% V. The refined parameters were used to calculate phase relationships, which were then compared with experimental results.The main interest was focused on the temperature and concentration regions of existence of the chromium-rich carbides M7C3 and M23C6 and Mo-rich carbides M6C and M2C. Results of experiments indicate that M7C3 carbide replaces M23C6 carbide in the temperature region between 773 and 873 K. Similar behavior was also found for molybdenum-rich phases M6C and M2C. Some modifications of existing thermodynamic parameters in the low-temperature region, as well as the establishment of some new parameters, were necessary to obtain reasonable agreement between theoretical and experimental results.
Related content


By Maugis P. Lacaze J. Besson R. Morillo J.
Metallurgical and Materials Transactions A, Vol. 37, Iss. 12, 2006-12 ,pp. :




A Study of the Iron-Rich Portion of the Fe-U Phase Diagram
By Michaud G.G.
Canadian Metallurgical Quarterly, Vol. 5, Iss. 4, 1966-10 ,pp. :


C-Cr-Fe-Mo-V (Carbon-Chromium-Iron-Molybdenum-Vanadium)
By Raghavan V.
Journal of Phase Equilibria & Diffusion, Vol. 28, Iss. 3, 2007-06 ,pp. :