Experimental investigation of the failure envelope of unidirectional carbon-epoxy composite under high strain rate transverse and off-axis tensile loading

Author： Kuhn Peter

Publisher： Edp Sciences

E-ISSN： 2100-014x|94|issue|01040-01040

ISSN： 2100-014x

Source： EPJ Web of Conference, Vol.94, Iss.issue, 2015-09, pp. : 01040-01040

Access to resources Favorite

Disclaimer: Any content in publications that violate the sovereignty, the constitution or regulations of the PRC is not accepted or approved by CNPIEC.

Previous Menu Next

Abstract

The mechanical response of the carbon-epoxy material system HexPly IM7-8552 was investigated under transverse tension and combined transverse tension / in-plane shear loading at quasi-static and dynamic strain rates. The dynamic tests of the transverse tension and off-axis tension specimens were carried out on a split-Hopkinson tension bar system, while the quasi-static reference tests were performed on a standard electro-mechanical testing machine. Digital image correlation was used for data reduction at both strain rate regimes. For the high rate tests, the strain rate in loading direction was adjusted to reach approximately the same strain rate value in the fracture plane for each specimen. The measured axial strengths were transformed from the global coordinate system into the combined transverse tension-shear stress space of the material coordinate system and compared with the Puck Mode A criterion for inter-fibre failure. A good correlation between the experimental data and the predicted failure envelopes was found for both investigated strain rate regimes.