A nonlocal damage mechanics approach to high temperature fatigue crack growth

Author： Zhixiong Q.   Shigeo T.   Katsumi T.  

Publisher： Elsevier

ISSN： 0013-7944

Source： Engineering Fracture Mechanics, Vol.53, Iss.4, 1996-03, pp. : 535-543

Disclaimer: Any content in publications that violate the sovereignty, the constitution or regulations of the PRC is not accepted or approved by CNPIEC.

Previous Menu Next

Abstract

Related content

The asymptotic study of fatigue crack growth based on damage mechanics

By Jun Z.   Xing Z.  

Engineering Fracture Mechanics, Vol. 50, Iss. 1, 1995-01 ,pp. : 131-141

Elsevier

Access to resources Recommend Favorite

Influence of foreign-object damage on crack initiation and early crack growth during high-cycle fatigue of Ti-6Al-4V

By Peters J.O.   Ritchie R.O.  

Engineering Fracture Mechanics, Vol. 67, Iss. 3, 2000-10 ,pp. : 193-207

Elsevier

Access to resources Recommend Favorite

Crack growth in alumina at high temperature

By Tran D.K.   Kobayashi A.S.   White K.W.  

Engineering Fracture Mechanics, Vol. 68, Iss. 2, 2001-02 ,pp. : 149-161

Elsevier

Access to resources Recommend Favorite

A fracture mechanics analysis of fatigue crack growth in a complex cross section

By Rifani A.I.   Grandt A.F.  

Engineering Failure Analysis, Vol. 3, Iss. 4, 1996-12 ,pp. : 249-265

Elsevier

Access to resources Recommend Favorite

A continuum damage mechanics model for void growth and micro crack initiation

By Dhar S.   Sethuraman R.   Dixit P.M.  

Engineering Fracture Mechanics, Vol. 53, Iss. 6, 1996-04 ,pp. : 917-928

Elsevier

Access to resources Recommend Favorite