Overload effects on corrosion fatigue crack initiation life and life prediction of aluminum notched elements under variable amplitude loading

Author： Zheng X. Wang R.

Publisher： Elsevier

ISSN： 0013-7944

Source： Engineering Fracture Mechanics, Vol.63, Iss.5, 1999-07, pp. : 557-572

Disclaimer: Any content in publications that violate the sovereignty, the constitution or regulations of the PRC is not accepted or approved by CNPIEC.

Previous Menu Next

Abstract

Related content

On the corrosion fatigue crack initiation model and expression of metallic notched elements

By Zheng X. Wang R.

Engineering Fracture Mechanics, Vol. 57, Iss. 6, 1997-08 ,pp. : 617-624

Elsevier

Access to resources Recommend Favorite

A stochastic model of fatigue crack propagation under variable-amplitude loading

By Ray A. Patankar R.

Engineering Fracture Mechanics, Vol. 62, Iss. 4, 1999-03 ,pp. : 477-493

Elsevier

Access to resources Recommend Favorite

Fatigue properties of jointed wood composites Part II Life prediction analysis for variable amplitude loading

By BOND I. P. ANSELL M. P.

Journal of Materials Science, Vol. 33, Iss. 16, 1998-08 ,pp. : 4121-4129

Springer Publishing Company

Access to resources Recommend Favorite

Closure effects on fatigue crack growth rates at constant and variable amplitude loading

By Mansson T. Oberg H. Nilsson F.

Engineering Fracture Mechanics, Vol. 71, Iss. 9, 2004-06 ,pp. : 1273-1288

Elsevier

Access to resources Recommend Favorite

Effect of pitting corrosion on fatigue crack initiation and fatigue life

By Rokhlin S.I. Kim J.-Y. Nagy H. Zoofan B.

Engineering Fracture Mechanics, Vol. 62, Iss. 4, 1999-03 ,pp. : 425-444

Elsevier

Access to resources Recommend Favorite