Flaking failure in rolling contact fatigue caused by indentations on mating surface (I) - Reproduction of flaking failure accompanied by cracks extending bi-directionally relative to the load-movement

Author： Fujii Y.   Maeda K.  

Publisher： Elsevier

ISSN： 0043-1648

Source： Wear, Vol.252, Iss.9, 2002-05, pp. : 787-798

Disclaimer: Any content in publications that violate the sovereignty, the constitution or regulations of the PRC is not accepted or approved by CNPIEC.

Previous Menu Next

Abstract

Related content

Flaking failure in rolling contact fatigue caused by indentations on mating surface (II) - Formation process of flaking failure accompanied by cracks extending bi-directionally relative to the load-movement

By Fujii Y.   Maeda K.  

Wear, Vol. 252, Iss. 9, 2002-05 ,pp. : 799-810

Elsevier

Access to resources Recommend Favorite

Flaking failure in rolling contact fatigue caused by indentations on mating surface (III) - Mechanism of crack growth in the direction opposite to the load-movement

By Fujii Y.   Maeda K.  

Wear, Vol. 252, Iss. 9, 2002-05 ,pp. : 811-823

Elsevier

Access to resources Recommend Favorite

A study of line defect fatigue failure of ceramic rolling elements in rolling contact

By Wang Y.   Hadfield M.  

Wear, Vol. 253, Iss. 9, 2002-11 ,pp. : 975-985

Elsevier

Access to resources Recommend Favorite

A model for rolling contact failure

By Jiang Y.   Sehitoglu H.  

Wear, Vol. 224, Iss. 1, 1999-01 ,pp. : 38-49

Elsevier

Access to resources Recommend Favorite

Boundary element analysis of surface initiated rolling contact fatigue cracks in wheel/rail contact systems

By Akama M.   Mori T.  

Wear, Vol. 253, Iss. 1, 2002-07 ,pp. : 35-41

Elsevier

Access to resources Recommend Favorite