Author： Hossain K. M. Zakir Chowdhury A. M. Sarwaruddin Haque M. E. Dafader N. C. Akhtar F.
Publisher： Taylor & Francis Ltd
ISSN： 0360-2559
Source： Polymer-Plastics Technology and Engineering, Vol.49, Iss.2, 2010-01, pp. : 136-140
Disclaimer: Any content in publications that violate the sovereignty, the constitution or regulations of the PRC is not accepted or approved by CNPIEC.
Abstract
Natural rubber latex and various concentration of natural antioxidant were blended in different ratios and irradiated at various absorbed doses by gamma rays from Co-60 source at room temperature. The aqueous extraction of Diospyros peregrina was used as natural antioxidant. It was found that the addition of different concentration of natural antioxidant into natural rubber latex improve the aging property of the film. Decreasing in tensile strength of rubber film with 10 phr natural antioxidant and 15 kGy radiation dose after 24 hours aging at 100°C was 9.34% compared to 13.89% for film without natural antioxidant. The tensile strength, tear resistance and modulus at 500% elongation of the rubber film were found to be optimum at 15 kGy radiation dose and with 10 phr natural antioxidant. Elongation at break, permanent set and swelling ratio decreases with the increasing absorbed radiation dose as well as the concentration of the natural antioxidant.
Access to resources
Recommend