Fatigue crack growth behaviour of 4130X steel in H2S environment

Author： Zhang Y. L.   Miao W.   Sun Z. Y.   Wang J.   Zeng Y. J.  

Publisher： Maney Publishing

ISSN： 1743-2782

Source： Corrosion Engineering, Science and Technology, Vol.44, Iss.6, 2009-12, pp. : 462-468

Disclaimer: Any content in publications that violate the sovereignty, the constitution or regulations of the PRC is not accepted or approved by CNPIEC.

Previous Menu Next

Abstract

Related content

Effect of H2S on stress corrosion cracking and hydrogen permeation behaviour of X56 grade steel in atmospheric environment

By Zheng C. B.   Huang Y. L.   Yu Q.   Huo C. Y.  

Corrosion Engineering, Science and Technology, Vol. 44, Iss. 2, 2009-04 ,pp. : 96-100

Maney Publishing

Access to resources Recommend Favorite

Effect of Ca(OH)2+NaCl Environment on Corrosion Fatigue Crack Growth in Rods Cold Drawn Eutectoid Steel

By Singh N.   Sanchez-Galvez V.  

British Corrosion Journal, Vol. 26, Iss. 2, 1991-01 ,pp. : 117-122

Maney Publishing

Access to resources Recommend Favorite

Corrosion behaviour of X52 pipeline steel in high H 2 S concentration solutions at temperatures ranging from 25癈 to 140癈

By Liu M.   Wang J.   Ke W.  

Corrosion Engineering, Science and Technology, Vol. 48, Iss. 5, 2013-08 ,pp. : 380-387

Maney Publishing

Access to resources Recommend Favorite

Electrochemistry of deformed smooth surfaces and short corrosion fatigue crack growth behaviour

By DMYTRAKH I. M.   AKID R.   MILLER K. J.  

British Corrosion Journal, Vol. 32, Iss. 2, 1997-01 ,pp. : 138-144

Maney Publishing

Access to resources Recommend Favorite

Effect of temperature on corrosion behaviour of X70 steel in high pressure CO 2 /SO 2 /O 2 /H 2 O environments

By Xiang Y   Wang Z   Li Z   Ni W D  

Corrosion Engineering, Science and Technology, Vol. 48, Iss. 2, 2013-04 ,pp. : 121-129

Maney Publishing

Access to resources Recommend Favorite