Formation of nickel aluminide/nickel hybrid coatings on alloy steels by two step process of nickel plating and low temperature pack aluminisation

Author： Xiang Z. D. Datta P. K.

Publisher： Maney Publishing

ISSN： 1743-2847

Source： Materials Science and Technology, Vol.25, Iss.6, 2009-06, pp. : 733-738

Disclaimer: Any content in publications that violate the sovereignty, the constitution or regulations of the PRC is not accepted or approved by CNPIEC.

Previous Menu Next

Abstract

The present study investigates the conditions required for forming a hybrid coating consisting of an outer nickel aluminide layer and an inner nickel layer on alloy steels. A commercial alloy steel of 9Cr–1Mo was used as a substrate. Electroless and electronickel plating processes were used to form an initial nickel layer on the steel. The AlCl₃ activated packs containing pure Al as a depositing source were then used to aluminise the nickel deposit at temperatures ≤650°C. The effect of phosphorus or boron content in the initial nickel layer deposited with the electroless nickel plating solutions using hypophosphite or boron–hydrogen compound as reducing agent was investigated in relation to the spallation tendency of the coating either immediately after the aluminising process or during the thermal annealing post-aluminising process. Under the aluminising conditions used, the outer nickel aluminide layer formed was Ni₂Al₃. For the electroplated nickel deposit, the growth kinetics of the outer Ni₂Al₃ layer during the pack aluminising process was found to obey the parabolic rate law with a parabolic rate constant being 12·67 μm at 650°C for 2 wt-%AlCl₃ activated pack containing 4 wt-% pure Al as a deposition source.