Cell compatibility of Co-Cr-Mo alloy treated with electrolytic in-process dressing grinding/thermal oxidation hybrid process

Author: Hiraga Ihori   Hamada Mihoshi   Komotori Jun   Mizutani Masayoshi  

Publisher: Inderscience Publishers

ISSN: 1746-9392

Source: International Journal of Nanomanufacturing, Vol.9, Iss.5-6, 2013-11, pp. : 486-495

Disclaimer: Any content in publications that violate the sovereignty, the constitution or regulations of the PRC is not accepted or approved by CNPIEC.

Previous Menu Next

Abstract

In order to improve cell compatibility of the Co-Cr-Mo alloys, an electrolytic in-process dressing (ELID) grinding and thermal oxidation (TO) hybrid process was performed. Surface roughness of specimens was measured by a non-contact type three-dimensional profilometer, and the elemental analysis of the treated surface was performed by a glow discharge optical emission spectrometer (GD-OES). To evaluate cell compatibility, a cell culturing assay was carried out. The surface roughness of all treated specimens was lower than that of the sliding parts of commercially applied artificial hip joints. Elemental analysis showed that the oxygen content from the surface of specimens treated with TO increased significantly with the increase in treating temperature. In particular, a region with a lower content of cobalt was observed at the ELID/TO hybrid-treated specimens with treated temperatures higher than 500°C. Moreover, the ELID/TO hybrid-treated specimens showed better cell compatibility than other specimens. This was because the levels of cobalt ions released from ELID/TO hybrid-treated specimens was lower than that of the others.

Related content