Synthesis and characterization of Ni–Al₂O₃ composite coatings containing different forms of alumina

Author： Aruna S. William Grips V. Rajam K.

ISSN： 0021-891X

Source： Journal of Applied Electrochemistry, Vol.40, Iss.12, 2010-12, pp. : 2161-2169

Disclaimer: Any content in publications that violate the sovereignty, the constitution or regulations of the PRC is not accepted or approved by CNPIEC.

Previous Menu Next

Abstract

Electrodeposited Ni–Al₂O₃ composite coatings were prepared using alumina powders synthesized from solution combustion method, precipitation method and a commercial source. Solution combustion synthesized alumina powder yielded α-phase; precipitation method yielded purely γ-phase; commercial alumina powder was a mixture of α-, δ- and γ-phases. A nickel sulfamate bath was used for electro-codeposition. The current densities (0.23 A dm⁻² for 20 h, 0.77 A dm⁻² for 6 h, 1.55 A dm⁻² for 3 h and 3.1 A dm⁻² for 1.5 h) and bath agitation speeds (100, 200, 600 and 1000 rpm) were varied. The pH variations of the bath were higher during the electrodeposition of combustion synthesized alumina. The effect of different forms of alumina particles on the microhardness and microstructure of the nickel composite coating was studied. Composite coating containing combustion synthesized alumina particles was found to have higher microhardness (550 HK). It was found that at lower agitation speed (100 rpm), bigger particles were incorporated and at higher agitation speed (1000 rpm), smaller particles were incorporated. The area fraction of alumina particles incorporated in nickel matrix was highest for commercial alumina (24%). This study shows that it is not suffice to take just the current density and stirring speeds into account to explain the properties of the coatings but also to take into account the source of particles and their properties.