The effect of PO_2,5 and AlO_1,5 additions on structural changes and crystallization behavior of SiO₂-TiO₂ sol-gel derived glasses and thin films

Author： Vasconcelos H.

Publisher： Springer Publishing Company

ISSN： 0928-0707

Source： Journal of Sol-Gel Science and Technology, Vol.55, Iss.1, 2010-07, pp. : 126-133

Disclaimer: Any content in publications that violate the sovereignty, the constitution or regulations of the PRC is not accepted or approved by CNPIEC.

Previous Menu Next

Abstract

SiO₂-TiO₂-PO_2,5 (STP) and SiO₂-TiO₂-AlO_1,5 (STA) glasses were prepared by sol-gel processing. Their infrared absorption spectra (IR), differential thermal analysis curves (DTA) and X-ray diffraction patterns (XRD) have been recorded. In the SiO₂-TiO₂ system, the chemical homogeneity of the sol-gel glass could be evaluated by the relative concentration of Si-O-Ti heterocondensation comparing to Si-O-Si homocondensation. For the STA system, a gradual decrease of the Si-O-Ti/Si-O-Si band ratio (based on IR spectra) with the addition of Al₂O₃ is observed, with the simultaneous formation of Si-O-Al and Ti-O-Al bounds, i.e Al₃⁺ ions are dissolved in the SiO₂-TiO₂ glass matrix and do not promote glass-in-glass phase-separation in the composition range of 0–15 mol% AlO_1.5. In the STP system, on the other hand, P=O bond IR stretch in the ternary glasses indicates that P=O free PO₂O_2/2⁻ tetrahedra are formed, rather than the double bonded POO_3/2 tetrahedra that usually occur in binary SiO₂-P₂O₅ glasses. It can be concluded that SiO₂-TiO₂-P₂O₅ glass separates into a SiO₂-rich phase and a TiO₂(P₂O₅)-rich phase. During heat-treatment in STA system only anatase precipitates, even at T ~ 1,000 °C, while in for STP, anatase (TiO₂) or (TiO)₂P₂O₇ (TOP) crystals precipitate at ~600 °C, depending on the P₂O₅ concentration. The major crystal phase, cristobalite, precipitated at ~1,000 °C and at ~1,200 °C, the P-containing phase melts.