The Effect of Solution Heat Treatment and Quenching Rates on Mechanical Properties and Microstructures in AlSiMg Foundry Alloys

Author： Pedersen L. Arnberg L.

Publisher： Springer Publishing Company

ISSN： 1543-1940

Source： Metallurgical and Materials Transactions A, Vol.32, Iss.3, 2001-03, pp. : 525-532

Disclaimer: Any content in publications that violate the sovereignty, the constitution or regulations of the PRC is not accepted or approved by CNPIEC.

Previous Menu Next

Abstract

Four common AlSiMg foundry alloys have been solution heat treated at 813 K, quenched, and immediately aged at 423 K for up to 240 minutes. The mechanical properties are found to be related to the amount of Mg and Si in the alloys. A high strength is obtained after only 60 minutes of solution heat treatment, indicating that the solid solution is rapidly saturated on Mg and Si. The ductility is very much related to the amount of silicon present and the refinement of the silicon crystals within the eutectic areas, since silicon crystals are observed to crack when load is applied. Thus, a well-modified structure is the best way to obtain high ductility. Reduced quenching rates after solution heat treatment lead to a lower strength, since a lower number of hardening β′-Mg₂Si precipitates are formed. The ductility of alloys with 0.6 wt pct Mg is increased with a reduced quenching rate. A more ductile matrix corresponding to the lower amount of hardening precipitates can explain this. Alloys with 0.2 wt pct Mg remain relatively unchanged. A hypothesis that may explain this phenomenon is the precipitation of brittle silicon or formation of coarse Mg2Si within the dendrites.