Optimization of Mechanical Properties of High-Carbon Pearlitic Steels with Si and V Additions

Author： Han K. Edmonds D.V. Smith G.D.W.

ISSN： 1543-1940

Source： Metallurgical and Materials Transactions A, Vol.32, Iss.6, 2001-06, pp. : 1313-1324

Disclaimer: Any content in publications that violate the sovereignty, the constitution or regulations of the PRC is not accepted or approved by CNPIEC.

Previous Menu Next

Abstract

Systematic research has been undertaken on the effects of single and combined additions of vanadium and silicon on the mechanical properties of pearlitic steels being developed for wire rod production. Mechanical test results demonstrate that the alloy additions are beneficial to the mechanical properties of the steels, especially the tensile strength. Silicon strengthens pearlite mainly by solid-solution strengthening of the ferrite phase. Vanadium increases the strength of pearlite mainly by precipitation strengthening of the pearlitic ferrite. When added separately, these elements produce relatively greater strengthening at higher transformation temperatures. When added in combination the behavior is different, and substantial strength increments are produced at all transformation temperatures studied (550 °C to 650 °C). The addition of silicon and vanadium to very-high-carbon steels (>0.8 wt pct C) also suppresses the formation of a network of continuous grain-boundary cementite, so that these hypereutectoid materials have high strength coupled with adequate ductility for cold drawing. A wire-drawing trial showed that total drawing reductions in area of 90 pct could be obtained, leading to final tensile strengths of up to 2540 MPa in 3.3-mm-diameter wires.