The Dy-Zn Phase Diagram

Author： Saccone A. Cardinale A. M. Delfino S. Ferro R.

ISSN： 1543-1940

Source： Metallurgical and Materials Transactions A, Vol.34, Iss.3, 2003-03, pp. : 743-750

Disclaimer: Any content in publications that violate the sovereignty, the constitution or regulations of the PRC is not accepted or approved by CNPIEC.

Previous Menu Next

Abstract

The dysprosium-zinc phase diagram has been investigated over its entire composition range by using differential thermal analysis, (DTA) metallographic analysis, X-ray powder diffraction, and electron probe microanalysis (EPMA). Seven intermetallic phases have been found and their structures confirmed. DyZn, DyZn₂, Dy₁₃Zn₅₈, and Dy₂Zn₁₇ melt congruently at 1095 °C, 1050 °C, 930 °C, and 930 °C, respectively. DyZn₃, Dy₃Zn₁₁, and DyZn₁₂ form through peritectic reactions at 895 °C, about 900 °C and 685 °C, respectively. Four eutectic reactions occur at 850 °C and 30.0 at pct Zn (between (Dy) and DyZn), 990 °C and 60.0 at pct Zn (between DyZn and DyZn₂), 885 °C and 76.0 at pct Zn (between DyZn₃ and Dy₃Zn₁₁), and 875 °C and 85.0 at pct Zn (involving Dy₁₃Zn₅₈ and Dy₂Zn₁₇). The Dy-rich end presents a catatectic equilibrium; a degenerate invariant effect has been found in the Zn-rich region. The phase equilibria of the Dy-Zn alloys are discussed and compared with those of the other known RE-Zn systems (RE = rare earth metal) in view of the regular change in the relative stabilities of the phases across the lanthanide series