Author: Hagiwara Masuo Araoka Aya Yang Seung Jin Emura Satoshi Nam Soo Woo
Publisher: Springer Publishing Company
ISSN: 1543-1940
Source: Metallurgical and Materials Transactions A, Vol.35, Iss.7, 2004-07, pp. : 2161-2170
Disclaimer: Any content in publications that violate the sovereignty, the constitution or regulations of the PRC is not accepted or approved by CNPIEC.
Abstract
The room-temperature tensile and high-cycle fatigue (HCF) behavior of orthorhombic Ti-22Al-27Nb alloy with varying lamellar morphology was investigated. Varying lamellar morphology was produced by changing the cooling rate after annealing in the single B2 phase region. A slower cooling rate of 0.003 K/s, for example, resulted in several large packets or colonies of similarly aligned O-phase lamellae and a nearly continuous massive α2 phase at the prior B2 grain boundaries, while a faster cooling rate of 0.1 K/s led to the refinement of colony sizes and the O-phase lamellae. The interface of O-phase lamellae and B2 phases was semicoherent. Water quenching produced a very fine tweed-like microstructure with a thin continuous O phase at the prior B2 grain boundaries. The 0.2 pct yield stress, tensile strength, and HCF strength increased with increasing cooling rate. For example, the tensile strength and HCF strength at 107 cycles of 0.003 and 0.1 K/s-cooled were 774 and 450 MPa, and 945 and 620 MPa, respectively. Since the fatigue ratio, which is the ratio of HCF strength at 107 cycles to tensile strength, did not show a constant value, but instead increased with increasing cooling rate, part of the fatigue improvement was the result of improved resistance to fatigue associated with the microstructural refinement of the lamellar morphology. Fatigue failure occurred by the subsurface initiation, and every initiation site was found to contain a flat facet. Concurrent observation of the fatigue initiation facet and the underlying microstructure revealed that the fatigue crack initiated in a shear mode across the colony, irrespective of colony size, indicating that the size of the initiation facet corresponded to that of the colony. Therefore, the colony size is likely a major controlling factor in determining the degree of fatigue improvement due to the microstructural refinement of lamellar morphology. For the water-quenched specimens, fatigue crack initiation appeared to be associated with shear cracking along the boundary between the continuous grain boundary O phase and the adjacent prior B2 grain.
Related content
By Emura Satoshi Yang Seung Jin Hagiwara Masuo
Metallurgical and Materials Transactions A, Vol. 35, Iss. 9, 2004-09 ,pp. :
By Draper S. Nathal M. Lerch B. Pereira J. Austin C. Erdmann O.
Metallurgical and Materials Transactions A, Vol. 32, Iss. 11, 2001-11 ,pp. :