LiMn₂O₄ CATHODE MATERIAL FOR LITHIUM ION BATTERIES

Author： SENGUPTA S. ROY R.R. McLEAN A. DASGUPTA S.

ISSN： 0008-4433

Source： Canadian Metallurgical Quarterly, Vol.45, Iss.3, 2006-01, pp. : 341-346

Disclaimer: Any content in publications that violate the sovereignty, the constitution or regulations of the PRC is not accepted or approved by CNPIEC.

Previous Menu Next

Abstract

A solution based method was used for the synthesis of lithium manganese oxide using polyvinyl alcohol (PVA) as a chelating agent. It was found from thermogravimetric analysis/differential scanning calorimetry (TGA/DSC) analysis that at about 220 °C, the synthesis reaction was completed. The precursor powders obtained were annealed between 250 and 600 °C from 2 to 8 hours to obtain pure spinel oxides. The morphology of the synthesized materials consisted of submicron sized particles agglomerated inside a network structure. At the discharge rate of 1 C, the highest discharge capacity obtained was 118 mAh/g; this was achieved with material annealed at 600 °C for 8 hours.On a utilisé une méthode à base de solution pour la synthèse de l’oxyde de manganèselithium en utilisant de l’alcool polyvinylique (PVA) comme agent complexant. À partir de l’analyse thermogravimétrique et de l’analyse calorimétrique à balayage différentiel (TGA/DSC), on a trouvé que la réaction de synthèse était complétée à environ 220 °C. Les poudres précurseurs obtenues ont été recuites entre 250 et 600 °C, de 2 à 8 heures, pour obtenir des oxydes de spinelle purs. La morphologie des matériaux synthétisés consistait en particules de taille submicronique agglomérées à l’intérieur d’une structure réticulaire. À l’intensité de décharge de 1 C, l’intensité la plus élevée obtenue pour le courant de décharge était de 118 mAh/g; on a obtenu cela avec le matériau recuit à 600 °C pendant 8 heures.