Effect of Cu strike coating on adhesion between Cu–Sn coated steel and rubber

Author： Banerjee Atanu   Dutta Monojit   Bhowmick Anil K.   Laha Tapas  

Publisher： Taylor & Francis Ltd

ISSN： 1568-5616

Source： Journal of Adhesion Science and Technology, Vol.28, Iss.16, 2014-08, pp. : 1610-1628

Disclaimer: Any content in publications that violate the sovereignty, the constitution or regulations of the PRC is not accepted or approved by CNPIEC.

Previous Menu Next

Related content

Adhesion between rubber compounds and ternary-alloy-coated steel cords, Part I: effect of cobalt plating amount in ternary-alloy-coated steel cords

By Jeon Gyung Soo  

Journal of Adhesion Science and Technology, Vol. 19, Iss. 6, 2005-05 ,pp. : 445-465

Taylor & Francis Ltd

Access to resources Recommend Favorite

Adhesion between polyurethane coating and EPDM rubber compound

By Ginic-Markovic Milena   Choudhury Namita Roy   Dimopoulos Maria   Matisons Janis  

Journal of Adhesion Science and Technology, Vol. 18, Iss. 5, 2004-05 ,pp. : 575-596

Taylor & Francis Ltd

Access to resources Recommend Favorite

Adhesion between rubber compounds and ternary-alloy-coated steel cords. Part II: Effects of sulfur and cobalt salt in rubber compounds

By Jeon Gyung Soo   Kang Ung Il   Jeong Seung Won   Choi Seok Ju   Kim Seok Ho  

Journal of Adhesion Science and Technology, Vol. 19, Iss. 15, 2005-12 ,pp. : 1325-1348

Taylor & Francis Ltd

Access to resources Recommend Favorite

Adhesion Between Rubber Compounds Containing Various Adhesion Promoters and Brass-Plated Steel Cords. Part II. Effect of Accelerator Loading in Rubber Compounds

By Jeon Gyung Soo  

Journal of Adhesion Science and Technology, Vol. 22, Iss. 12, 2008-08 ,pp. : 1255-1284

Taylor & Francis Ltd

Access to resources Recommend Favorite

Adhesion Between Rubber Compounds Containing Various Adhesion Promoters and Brass-Plated Steel Cords. Part I. Effect of Sulfur Loading in Rubber Compounds

By Jeon Gyung Soo  

Journal of Adhesion Science and Technology, Vol. 22, Iss. 12, 2008-08 ,pp. : 1223-1253

Taylor & Francis Ltd

Access to resources Recommend Favorite