Growth of High-Density Zinc Oxide Nanorods on Porous Silicon by Thermal Evaporation

Author： Rusli Nurul Izni Tanikawa Masahiro Mahmood Mohamad Rusop Yasui Kanji Hashim Abdul Manaf

Publisher： MDPI

E-ISSN： 1996-1944|5|12|2817-2832

ISSN： 1996-1944

Source： Materials, Vol.5, Iss.12, 2012-12, pp. : 2817-2832

Disclaimer: Any content in publications that violate the sovereignty, the constitution or regulations of the PRC is not accepted or approved by CNPIEC.

Previous Menu Next

Abstract

The formation of high-density zinc oxide (ZnO) nanorods on porous silicon (PS) substrates at growth temperatures of 600–1000 °C by a simple thermal evaporation of zinc (Zn) powder in the presence of oxygen (O₂) gas was systematically investigated. The high-density growth of ZnO nanorods with (0002) orientation over a large area was attributed to the rough surface of PS, which provides appropriate planes to promote deposition of Zn or ZnO_x seeds as nucleation sites for the subsequent growth of ZnO nanorods. The geometrical morphologies of ZnO nanorods are determined by the ZnO_x seed structures, i.e., cluster or layer structures. The flower-like hexagonal-faceted ZnO nanorods grown at 600 °C seem to be generated from the sparsely distributed ZnO_x nanoclusters. Vertically aligned hexagonal-faceted ZnO nanorods grown at 800 °C may be inferred from the formation of dense arrays of ZnO_x clusters. The formation of disordered ZnO nanorods formed at 1000 °C may due to the formation of a ZnO_x seed layer. The growth mechanism involved has been described by a combination of self-catalyzed vapor-liquid-solid (VLS) and vapor-solid (VS) mechanism. The results suggest that for a more precise study on the growth of ZnO nanostructures involving the introduction of seeds, the initial seed structures must be taken into account given their significant effects.