Enhancing the Phase Conversion of Hydroxyapatite from Calcium Sulphate Hemihydrate by Hydrothermal Reaction

E-ISSN： 1662-9795|2018|766|288-293

ISSN： 1013-9826

Source： Key Engineering Materials, Vol.2018, Iss.766, 2018-06, pp. : 288-293

Disclaimer: Any content in publications that violate the sovereignty, the constitution or regulations of the PRC is not accepted or approved by CNPIEC.

Previous Menu Next

Abstract

Hydroxyapatite (HA) is a well-known biocompatible material which is widely used in orthopedic and dental applications. Because its chemical structure is similar to the human bone so it is compatible to use as a based materials in drug delivery system for treatment of bone infection diseases. In this research we focused on fabrication of HA sphere shape by three dimension printing using calcium sulphate hemihydrate (CaSO₄·0.5H₂O) as a starting material, then the as-three dimension printed CaSO₄·0.5H₂O spheres were hydrothermally treated in 1M disodium hydrogenphosphate (Na₂HPO₄) at 100°C-180°C for 2-8 hr. The reaction was taken place and the conversion of CaSO₄·0.5H₂O was gradually changed to Ca₁₀(PO₄)₆(OH)₂. Phase analysis by X-ray diffraction indicated that monetite (CaHPO₄) was coexisted with HA when hydrothermally treated at pH 9 at low reaction temperature (lt;180°C). When the pH of 1M Na₂HPO₄ was adjusted to pH 11, 180°C for 6 hr, the as-three dimension printed calcium sulphate hemihydrate spheres were completely converted to HA spheres without any destruction of the sphere shape. This is confirmed that hydrothermal reaction could enhance the phase conversion of HA and the conversion time was four times faster than the normal conversion.