Wave absorption control in the new designed photonic metamaterials with artificial opal

E-ISSN： 2261-236x|178|issue|04004-04004

ISSN： 2261-236x

Source： MATEC Web of conference, Vol.178, Iss.issue, 2018-07, pp. : 04004-04004

Disclaimer: Any content in publications that violate the sovereignty, the constitution or regulations of the PRC is not accepted or approved by CNPIEC.

Previous Menu Next

Abstract

Photonic metamaterials consisting of artificial opal with magnetic inclusions were considered, used in controllable microwave electronic devices. The analyzed structures consist of matrices of SiO₂ nanospheres (diameter 200 - 400 nm) with included clusters of ferrite spinels (Mn_xCo_0.6-xZn_0.4Fe₂O₄, Ni_xCo_0.6-xZn_0.4Fe₂O₄, La_xCo_0.6-xZn_0.4Fe₂O₄, Nd_xCo_0.6-xZn_0.4Fe₂O₄) in interspherical nanospacing (4 ÷ 7% concentration). The ellipsoidal clusters are polycrystalline, with spatial dimensions of 20 – 30 nm and grains of 5 – 12 nm. A controlled wave absorption was obtained in these high inductivity structures. Evolution of the wave attenuation coefficient, α[dB/m], in function of the applied magnetic field and particle inclusion size, for different content of the magnetic ions in the ferrite inclusion, have been determined at frequencies around the samples ferromagnetic resonance, by structural simulation. The test configuration was: sample inside the rectangular waveguide, mode TE₁₀, in the frequency range 24 ÷ 40 GHz. The polarizing magnetic field for the ferrites was tested in the range of 0 ÷ 20 kOe and minimized by modifying the structure. The metamaterial design optimization was realized, controllable by different parameters at structure level. The ferromagnetic resonance influence on the control process was pointed out and also the particular results and effects which can be induced by the resonant behavior.