Biaxial Deformation of the Magnesium Alloy AZ80

ISSN： 1543-1940

Source： Metallurgical and Materials Transactions A, Vol.44, Iss.7, 2013-07, pp. : 2970-2983

Disclaimer: Any content in publications that violate the sovereignty, the constitution or regulations of the PRC is not accepted or approved by CNPIEC.

Previous Menu Next

Abstract

The multiaxial deformation of magnesium alloys is important for developing reliable, robust models for both the forming of components and also analysis of in-service performance of structures, for example, in the case of crash worthiness. The current study presents a combination of unique biaxial experimental tests and biaxial crystal plasticity simulations using a visco-plastic self-consistent (VPSC) formulation conducted on a relatively weak AZ80 cast texture. The experiments were conducted on tubular samples which are loaded in axial tension or compression along the tube and with internal pressure to generate hoop stresses orthogonal to the axial direction. The results were analyzed in stress and strain space and also in terms of the evolution of crystallographic texture. In general, it was found that the VPSC simulations matched well with the experiments. However, some differences were observed for cases where basal 〈a〉 slip and $$ left{ {10bar{1}2} right} $$ extension twinning were in close competition such as in the biaxial tension quadrant of the plastic potential. The evolution of texture measured experimentally and predicted from the VPSC simulations was qualitatively in good agreement. Finally, experiments and VPSC simulations were conducted on a second AZ80 material which had a stronger initial texture and a higher level of mechanical anisotropy. In the previous case, the agreement between experiments and simulations was good, but a larger difference was observed in the biaxial tension quadrant of the plastic potential.