Synthesis, Characterization, and Formation Process of Na-X Zeolite from Coal Fly Ash

ISSN： 1064-7562

Source： Journal of Materials Synthesis and Processing, Vol.10, Iss.3, 2002-05, pp. : 143-148

Disclaimer: Any content in publications that violate the sovereignty, the constitution or regulations of the PRC is not accepted or approved by CNPIEC.

Previous Menu Next

Abstract

Using the SiO₂ and Al₂O₃ components of the amorphous phase in coal fly ash (Fa), Fa was converted to Na-X zeolites in NaOH-NaAlO₂ solutions by stirring at 35°C for 72 hr and then aging at 85°C for a given period. The molar ratio SiO₂/Al₂O₃ of the starting materials was controlled from 2.0 to 13.2. The resulting materials were characterized by various means. Increasing the SiO₂/Al₂O₃ ratio of the starting material increased the degree of crystallinity of faujasite, exhibiting a maximum at SiO₂/Al₂O₃ = 8.0. The faujasite formed was identified as Na-X zeolite with Si/Al = 1.20. The amorphous phase in Fa was dissolved during the stirring to form a precursor of zeolite, such as amorphous aluminosilicate. The Na-X zeolite was formed by aging for 24 hr, and the degree of crystallinity of this material was increased with the increasing aging period. The cation exchange capacity and specific surface area were increased with the increasing degree of crystallinity of the Na-X zeolites.