Creep Behavior of Bi-Containing Lead-Free Solder Alloys

ISSN： 1543-186X

Source： Journal of Electronic Materials, Vol.41, Iss.2, 2012-02, pp. : 190-203

Disclaimer: Any content in publications that violate the sovereignty, the constitution or regulations of the PRC is not accepted or approved by CNPIEC.

Previous Menu Next

Abstract

The creep behavior of Sn-3.0Ag-0.5Cu (SAC305), Sn-3.4Ag-1.0Cu-3.3Bi (SAC-Bi), and Sn-3.4Ag-4.8Bi (SnAg-Bi, all wt.%) was studied in constant-stress creep tests from room temperature to 125°C. The alloys were tested in two microstructural conditions. As-cast alloys had a composite eutectic-primary Sn structure, while in aged alloys the eutectic regions were replaced by a continuous Sn matrix with coarsened intermetallic (Cu₆Sn₅ and Ag₃Sn) particles. After aging, Bi in SAC-Bi and SnAg-Bi was found as precipitates at grain boundaries and grain interiors. The creep resistance of of-cast SAC305 was higher than that of as-cast Bi-containing alloys, but after aging the SAC305 had the lowest creep resistance. The creep strain rates in SAC-Bi and SnAg-Bi were much less affected by aging. The apparent activation energy for creep was also changed more for SAC305 than for the other two alloys. The creep behavior of SAC-Bi and SnAg-Bi can be understood by considering the solubility of Bi in Sn. The difference in creep behavior between as-cast and aged SAC-Bi is greatly reduced when room-temperature test results are excluded from analysis. This suggests that the strongest influence on creep in these alloys is due to Bi solute interaction with moving dislocations during deformation.