A comparative study of three adhesion tests (EN 582, similar to ASTM C633, LASAT (LASer Adhesion Test), and bulge and blister test) performed on plasma sprayed copper deposited on aluminium 2017 substrates

Author： Arrigoni M.   Barradas S.   Braccini M.   Dupeux M.   Jeandin M.   Boustie M.   Bolis C.   Berthe L.  

Publisher： Taylor & Francis Ltd

ISSN： 1568-5616

Source： Journal of Adhesion Science and Technology, Vol.20, Iss.5, 2006-04, pp. : 471-487

Disclaimer: Any content in publications that violate the sovereignty, the constitution or regulations of the PRC is not accepted or approved by CNPIEC.

Previous Menu Next

Abstract

Related content

Adhesion (fracture energy) of electropolymerized poly(n-octyl maleimide-co-styrene) coatings on copper substrates using a constrained blister test

By Liang Jeng-Li  

Journal of Adhesion Science and Technology, Vol. 7, Iss. 8, 1993-01 ,pp. : 869-884

Taylor & Francis Ltd

Access to resources Recommend Favorite

The constrained blister test for the energy of interfacial adhesion

By Napolitano M.J.   Chudnovsky A.   Moet A.  

Journal of Adhesion Science and Technology, Vol. 2, Iss. 1, 1988-01 ,pp. : 311-323

Taylor & Francis Ltd

Access to resources Recommend Favorite

Improvements of the peel test for adhesion evaluation of thin metallic films on polymeric substrates

By Hagemeyer A.  

Journal of Adhesion Science and Technology, Vol. 8, Iss. 1, 1994-01 ,pp. : 29-40

Taylor & Francis Ltd

Access to resources Recommend Favorite

A clamped punch-loaded blister test for adhesion: a lumped parameter model and the bending-to-stretching behavior

By Feng Luyi   Li Xiwen   Shi Tielin  

Journal of Adhesion Science and Technology, Vol. 29, Iss. 16, 2015-08 ,pp. : 1733-1744

Taylor & Francis Ltd

Access to resources Recommend Favorite

The use of stimulated boundary gas release for determination of the adhesion of thin films by the blister test

By Borisenko Yu N.   Gritsyna V.T.   Ivko T.V.  

Journal of Adhesion Science and Technology, Vol. 9, Iss. 11, 1995-01 ,pp. : 1413-1426

Taylor & Francis Ltd

Access to resources Recommend Favorite