Abrasive wear characteristics of coating area of low carbon steel surface alloyed through tungsten inert gas welding process

Author： Korkut M. H. Gök M. S.

Publisher： Maney Publishing

ISSN： 1743-2944

Source： Surface Engineering, Vol.25, Iss.7, 2009-10, pp. : 517-525

Disclaimer: Any content in publications that violate the sovereignty, the constitution or regulations of the PRC is not accepted or approved by CNPIEC.

Previous Menu Next

Abstract

Low carbon steel surfaces were alloyed with composite powders using the tungsten inert gas welding method. After the alloying process, the effects of welding parameters, such as energy input, progress speed and coating thickness on the microstructural characteristics of the alloyed samples were examined. In the experimental investigation, a low carbon steel surface was alloyed with austenitic stainless steel powder and austenitic stainless steel composites mixed with 4·5% Co, Mo and Ti particles respectively. Following surface alloying, conventional characterisation techniques, such as optical microscopy, scanning electron microscopy, energy dispersive spectrograph and X-ray diffraction, were used to study the microstructure of the alloyed zone. Hardness measurements were also performed across the alloyed zone. Examination of the microstructure revealed the presence of M₂₃C₆ carbides, solid melt phases, and intermetallic phases, such as Ni₃Ti, depending on the alloying element in the composite. As the amount of the reinforcing material increased, the saturation rates for the samples decreased, while their hardness increased. The abrasive wear tests conducted revealed that temperature input plays a significant role on the microstructure characteristics, which positively affected the abrasive wear values of the samples. Consequently, the tungsten inert gas welding method was successfully used for the surface alloying of low carbon steels.