On the development of a new pre-weld thermal treatment procedure for preventing heat-affected zone (HAZ) liquation cracking in nickel-base IN 738 superalloy

Author： Ola O.T.   Ojo O.A.   Chaturvedi M.C.  

Publisher： Taylor & Francis Ltd

ISSN： 1478-6443

Source： Philosophical Magazine, Vol.94, Iss.29, 2014-10, pp. : 3295-3316

Disclaimer: Any content in publications that violate the sovereignty, the constitution or regulations of the PRC is not accepted or approved by CNPIEC.

Previous Menu Next

Related content

Solution Heat Treatment of the Single Crystal Nickel‐Base Superalloy CMSX‐4 Fabricated by Selective Electron Beam Melting

By  

ADVANCED ENGINEERING MATERIALS (ELECTRONIC), Vol. 17, Iss. 10, 2015-10 ,pp. : 1486-1493

John Wiley & Sons Inc

Access to resources Recommend Favorite

Solution Heat Treatment of the Single Crystal Nickel‐Base Superalloy CMSX‐4 Fabricated by Selective Electron Beam Melting

By  

ADVANCED ENGINEERING MATERIALS (ELECTRONIC), Vol. 1438-1656, Iss. 10, 2015-10 ,pp. : 1486-1493

John Wiley & Sons Inc

Access to resources Recommend Favorite

Long-Term Gamma Prime Phase Stability after Various Heat Treatment Conditions with Temperature Dropping during Solution Treatment in Cast Nickel Base Superalloy, Grade Inconel-738

By  

Materials Science Forum, Vol. 2017, Iss. 891, 2017-04 ,pp. : 420-425

Trans Tech Publications

Access to resources Recommend Favorite

Experimental investigation and life prediction of hot corrosion pre‐exposure on low‐cycle fatigue of a directionally solidified nickel‐base superalloy

By  

FATIGUE & FRACTURE OF ENGINEERING MATERIALS AND STRUCTURES, Vol. 38, Iss. 10, 2015-10 ,pp. : 1155-1166

John Wiley & Sons Inc

Access to resources Recommend Favorite

Microstructures of a single-crystal nickel-base superalloy after thermo-mechanical fatigue

By Wang Y. C.   Li S. X.   Zhou L.   Ai S. H.   Liu F.   Zhang H.   Wang Z. G.  

Philosophical Magazine, Vol. 84, Iss. 31, 2004-11 ,pp. : 3335-3351

Taylor & Francis Ltd

Access to resources Recommend Favorite