Microstructure and thermal stability of arc-evaporated Cr-C-N coatings

Author: Almer J.  

Publisher: Taylor & Francis Ltd

ISSN: 1478-6443

Source: Philosophical Magazine, Vol.84, Iss.7, 2004-03, pp. : 611-630

Disclaimer: Any content in publications that violate the sovereignty, the constitution or regulations of the PRC is not accepted or approved by CNPIEC.

Previous Menu Next

Abstract

The role of C incorporation in the microstructure and thermal stability of arc-evaporated Cr-C-N coatings is explored via reactive growth in a mixed C 2 H 4 -N 2 environment. C is found to react more readily than N at both the Cr cathode and the coating surfaces, so that a C 2 H 4 -to-N 2 flow ratio of only 1% yields a C-to-N ratio of approximately 10% within the coatings. The as-deposited microstructures consist primarily of the δ-Cr(C, N) phase and possess high compressive residual stresses, which decrease with increasing C content. Post-deposition annealing up to 700°C results in depletion of lattice defects, and concomitant reductions in stress and coating hardness, together with phase transformations which suggest metastable phase formation during growth. Apparent activation energies for this lattice defect are found to be in the range expected for bulk diffusion of N and C (2.4-2.8 eV). The results suggest that inclusion of small amounts of C in this system offers the ability to reduce internal stresses while maintaining defect-related hardness increases, permitting growth of thicker and thus more wear-resistant coatings.