Deep levels, electrical and optical characteristics in SnTe-Doped GaSb Schottky Diodes

ISSN： 1543-186X

Source： Journal of Electronic Materials, Vol.25, Iss.11, 1996-11, pp. : 1790-1796

Disclaimer: Any content in publications that violate the sovereignty, the constitution or regulations of the PRC is not accepted or approved by CNPIEC.

Previous Menu Next

Abstract

The GaSb layers investigated were grown directly on GaAs substrates by molecular beam epitaxy (MBE) using SnTe source as the n-type dopant. By using admittance spectroscopy, a dominant deep level with the activation energy of 0.23-0.26 eV was observed and its concentration was affected by the Sb₄/Ga flux ratio in the MBE growth. A lowest deep-level concentration together with a highest mobility was obtained for GaSb grown at 550°C under a Sb₄/Ga beam equivalent pressure (BEP) ratio around 7, which should correspond to the lowest ratio to maintain a Sb-stabilized surface reconstruction. In the Hall measurement, an analysis of the temperature-dependent mobility shows that the ionized impurity concentration increases proportionally with the sample’s donor concentration, suggesting that the ionized impurity was introduced by an SnTe source. In addition, optical properties of an undoped p-, a lightly and heavily SnTe-doped GaSb layers were studied by comparing their photoluminescence spectra at 4.5K.