The effects of microstructure on crack initiation in liquid-metal environments

Author： Fernandes P.J.L.   Jones D.R.H.  

Publisher： Elsevier

ISSN： 1350-6307

Source： Engineering Failure Analysis, Vol.4, Iss.3, 1997-09, pp. : 195-204

Disclaimer: Any content in publications that violate the sovereignty, the constitution or regulations of the PRC is not accepted or approved by CNPIEC.

Previous Menu Next

Abstract

Related content

The effect of crack blunting in liquid metal environments on K IEAC determined by the rising load test

By Fernandes P.J.L.   Jones D.R.H.  

Engineering Failure Analysis, Vol. 3, Iss. 3, 1996-09 ,pp. : 227-230

Elsevier

Access to resources Recommend Favorite

The effects of diffusion on environmental stress crack initiation in PMMA

By Arnold J.C.  

Journal of Materials Science, Vol. 33, Iss. 21, 1998-11 ,pp. : 5193-5204

Springer Publishing Company

Access to resources Recommend Favorite

Overload effects on corrosion fatigue crack initiation life and life prediction of aluminum notched elements under variable amplitude loading

By Zheng X.   Wang R.  

Engineering Fracture Mechanics, Vol. 63, Iss. 5, 1999-07 ,pp. : 557-572

Elsevier

Access to resources Recommend Favorite

Crack initiation and growth in brittle bonds

By Jensen H.M.  

Engineering Fracture Mechanics, Vol. 70, Iss. 13, 2003-09 ,pp. : 1611-1621

Elsevier

Access to resources Recommend Favorite

Effects of additives on densification, microstructure and properties of liquid-phase sintered silicon carbide

By Sciti D.   Bellosi A.  

Journal of Materials Science, Vol. 35, Iss. 15, 2000-08 ,pp. : 3849-3855

Springer Publishing Company

Access to resources Recommend Favorite