Hydrogen embrittlement failure of hot dip galvanised high tensile wires

Author： Mukhopadhyay N.K. Sridhar G. Parida N. Tarafder S. Ranganath V.R.

Publisher： Elsevier

ISSN： 1350-6307

Source： Engineering Failure Analysis, Vol.6, Iss.4, 1999-08, pp. : 253-265

Disclaimer: Any content in publications that violate the sovereignty, the constitution or regulations of the PRC is not accepted or approved by CNPIEC.

Previous Menu Next

Abstract

Related content

Hydrogen embrittlement failure of (Sm,Dy,Gd)Co 5 permanent magnets

By Lukin A.A. Szymura Rabinovich Bala H. Zhuravlyev A.A.

Engineering Failure Analysis, Vol. 5, Iss. 4, 1998-12 ,pp. : 317-321

Elsevier

Access to resources Recommend Favorite

Characteristics of hydrogen embrittlement, stress corrosion cracking and tempered martensite embrittlement in high-strength steels

By Eliaz

Engineering Failure Analysis, Vol. 9, Iss. 2, 2002-04 ,pp. : 167-184

Elsevier

Access to resources Recommend Favorite

The Use of Crack-Tip Opening Displacement for Testing of the Hydrogen Embrittlement of High-Strength Steels

By Dietzel W.

Materials Science, Vol. 40, Iss. 6, 2004-11 ,pp. : 749-755

Springer Publishing Company

Access to resources Recommend Favorite

Micromechanical Aspects of Reversible Hydrogen Embrittlement

By Shvachko V.I.

Materials Science, Vol. 36, Iss. 4, 2000-07 ,pp. : 513-518

Springer Publishing Company

Access to resources Recommend Favorite

Damage due to hydrogen embrittlement and stress corrosion cracking

By Woodtli J. Kieselbach R.

Engineering Failure Analysis, Vol. 7, Iss. 6, 2000-12 ,pp. : 427-450

Elsevier

Access to resources Recommend Favorite