Author： Ma Ai-jie Chen Weixing Hou Yonggang
Publisher： Taylor & Francis Ltd
ISSN： 0360-2559
Source： Polymer-Plastics Technology and Engineering, Vol.51, Iss.15, 2012-11, pp. : 1578-1582
Disclaimer: Any content in publications that violate the sovereignty, the constitution or regulations of the PRC is not accepted or approved by CNPIEC.
Abstract
To further improve the thermal conductivity of epoxy resin, the multi-walled carbon nanotube/aluminum nitride (MWCNTs/AlN) hybrid filler was employed to prepare thermal conductivity MWCNTs/AlN/epoxy composite by casting process, and the silane coupling reagent of γ-glycidoxy propyl trimethoxy silane(KH-560) was also used to functionalize the surface of MWCNTs and/or AlN. Results revealed that, the thermal conductivity of epoxy resin was improved remarkably with the addition of MWCNTs/AlN hybrid filler, a higher thermal conductivity of 1.04 W/mK could be achieved with 29 wt% MWCNTs/AlN hybrid filler (4 wt% MWCNTs +25 wt% AlN), about 5 times higher than that of native epoxy resin. And the epoxy composite with 29 wt% MWCNTs/AlN hybrid filler possessed better thermal conductivity and mechanical properties than those of single 5 wt% MWCNTs or 40 wt% AlN. The thermal decomposition temperature of MWCNTs/AlN/epoxy composite was increased with the addition of MWCNTs/AlN hybrid filler. For given filler loading, surface treatment of MWCNTs and/or AlN by KH-560 exhibited a positive effect on the thermal conductivity of epoxy composite.
Related content
Access to resources
Recommend