Publisher: Trans Tech Publications
E-ISSN: 1662-9752|2017|898|1140-1147
ISSN: 0255-5476
Source: Materials Science Forum, Vol.2017, Iss.898, 2017-07, pp. : 1140-1147
Disclaimer: Any content in publications that violate the sovereignty, the constitution or regulations of the PRC is not accepted or approved by CNPIEC.
Abstract
Cu-15Ni-8Sn alloy is a spinodal hardened alloy which possesses excellent combination of strength, elastic modulus, corrosion resistance and wear resistance. Much concern focuses on the microstructures and properties of this wrought alloys after heat treatment, however, the microstructure feature of the alloy during hot plastic deformation processing is rarely declared. The microstructure evolution of the hot-extruded Cu-15Ni-8Sn alloy with different extrusion ratio were investigated by optical microscope, scanning electronic microscope, electron backscattered diffraction. The results showed that dynamic recrystallization occured during hot extrusion at extrusion ratio ranging from 6 to 17. With the increase of extrusion ratio, the fraction of recrystallized grain increased. However, the amount of discontinuous γ precipitates reduced. The cellular structure was observed to grow not only on grain boundaries but also in the coarsening annealing grains when the extrusion ratio was below 13. When extrusion ratio was 17, the discontinuous γ precipitates and the residual annealing grains were suppressed and some recrystallized grains grew up.
Related content




Microstructure Evolution and Mechanical Properties of Extruded Mg-Al-Zn-Sn Alloy Sheets
Materials Science Forum, Vol. 2017, Iss. 898, 2017-07 ,pp. :


By Xing L. Q. Eckert J. Loser W. Schultz L. Herlach D. M.
Philosophical Magazine. A. Physics of Condensed Matter. Defects and Mechanical Properties, Vol. 79, Iss. 5, 1999-05 ,pp. :